Lexan* LUX7189 is an injection moldable, high light reflectance FR grade. Contains non-brominated, non-chlorinated flame retardant systems, UV stabilized.

防火阻燃，抗紫外线，注塑级

Sabic LEXAN LUX7189物性表

Property

TYPICAL PROPERTIES ⁽¹⁾
MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 50 mm/min	610	kgf/cm2	ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min	530	kgf/cm2	ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min	6	%	ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min	110	%	ASTM D 638
Tensile Modulus, 50 mm/min	27500	kgf/cm2	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	990	kgf/cm2	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	27500	kgf/cm2	ASTM D 790
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	218	cm-kgf/cm	ASTM D 4812
Izod Impact, notched, 23°C	15	cm-kgf/cm	ASTM D 256
Izod Impact, notched, -30°C	10	cm-kgf/cm	ASTM D 256
Instrumented Impact Energy @ peak, 23°C	601	cm-kgf	ASTM D 3763
THERMAL	Value	Unit	Standard
Vicat Softening Temp, Rate B/50	140	°C	ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed	135	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	125	°C	ASTM D 648
CTE, -40°C to 40°C, flow	6.E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	6.5E-05	1/°C	ASTM E 831
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.3	-	ASTM D 792
Density	1.3	g/cm3	ASTM D 792
Mold Shrinkage, flow, 3.2 mm (5)	0.5 - 0.7	%	SABIC Method
Melt Flow Rate, 300°C/1.2 kgf	22	g/10 min	ASTM D 1238
FLAME CHARACTERISTICS	Value	Unit	Standard
UL Recognized, 94V-0 Flame Class Rating (3)	1.5	mm	UL 94
UL Recognized, 94-5VA Rating (3)	3	mm	UL 94
UL Recognized, 94-5VB Rating (3)	2.5	mm	UL 94

Source GMD, last updated:2014/11/03

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	120	°C
Drying Time	3 - 4	hrs
Drying Time (Cumulative)	48	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	270 - 295	°C
Nozzle Temperature	265 - 290	°C
Front - Zone 3 Temperature	270 - 295	°C
Middle - Zone 2 Temperature	260 - 280	°C
Rear - Zone 1 Temperature	250 - 270	°C
Mold Temperature	70 - 95	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	40 - 70	rpm
Shot to Cylinder Size	40 - 60	%
Vent Depth	0.025 - 0.076	mm

101
1010 111N
101R
101R-111
101R-701
103R-111
104R-111
104R-GY6A579
1125
1132T BK
1200HF-701
1200HI-701
120P(粉)
121 11012
121 BK2065S
121-111N
121R
121R BL9E026T
121R BL9E031T-8652951
121R BR9E0317
101-111
121R WH5AD27X
121R-11012
121R-111
121R-21051
121R-70291
121SRM 888
122R-111
123 GY3923T
123R WH6D034
123R WH8A467XL07
123R-100
123R-111
123R-112
123R-701
123R-GN
1243R-111
124R-111
131
131R-111
141-111N
1413T
1414 BK1A346
1414 HW3064
1414 WH9A320L
1414R RK1A0681
141R
141R BK