Global grade. LEXAN LUX2010T is an injection molding grade especially designed for manufacturing optical parts requiring excellent flow properties combined with very high transmission and color stability.

全球级。聚碳酸酯LUX2010T注塑级尤其是用于制造光学零件需要优秀的流动性加上很高的传输和颜色稳定性。

LEXAN LUX2010T物性表

Property

TYPICAL PROPERTIES ⁽¹⁾
MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 50 mm/min	630	kgf/cm2	ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min	640	kgf/cm2	ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min	7	%	ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min	130	%	ASTM D 638
Tensile Modulus, 50 mm/min	22300	kgf/cm2	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	990	kgf/cm2	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	24000	kgf/cm2	ASTM D 790
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	218	cm-kgf/cm	ASTM D 4812
Izod Impact, notched, 23°C	68	cm-kgf/cm	ASTM D 256
Izod Impact, notched, -30°C	8	cm-kgf/cm	ASTM D 256
Instrumented Impact Energy @ peak, 23°C	642	cm-kgf	ASTM D 3763
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	139	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	127	°C	ASTM D 648
CTE, -40°C to 95°C, flow	6.4E-05	1/°C	ASTM E 831
CTE, -40°C to 95°C, xflow	6.7E-05	1/°C	ASTM E 831
Vicat Softening Temp, Rate B/120	143	°C	ISO 306
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.2	-	ASTM D 792
Density	1.2	g/cm3	ASTM D 792
Mold Shrinkage on Tensile Bar, flow (2) (5)	0.6 - 0.9	%	SABIC Method
Melt Flow Rate, 300°C/1.2 kgf	38	g/10 min	ASTM D 1238
OPTICAL	Value	Unit	Standard
Light Transmission, 2.54 mm	>90	%	ASTM D 1003

Source GMD, last updated:2015/02/20

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	120	°C
Drying Time	3 - 4	hrs
Drying Time (Cumulative)	48	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	295 - 315	°C
Nozzle Temperature	290 - 310	°C
Front - Zone 3 Temperature	295 - 315	°C
Middle - Zone 2 Temperature	280 - 305	°C
Rear - Zone 1 Temperature	270 - 295	°C
Mold Temperature	70 - 95	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	40 - 70	rpm
Shot to Cylinder Size	40 - 60	%
Vent Depth	0.025 - 0.076	mm

500
500-7040
500-7388
500-739
500ECR BK6A237
500ECR BL6A237L
500ECR GY8002L
500ECR GY90200
500ECR WH
500ECR WH9A459L
500ECR-131/739
500ECR-739L BK
500ECR-BK
500R
500R-131
500R-731
500R-73234
500R-739
500R-73966
500R-13021
500R-GY
500R-V0
5030R-739
503R
503R-111
503R-131
503R-739
503R-834
503R-GY
505R
510
550R-739
5832C
5901R
732-999
752-336-001
752-732-999
7604
7677-RED
8414
89406LN
9010-1573 UV
915AU BK1E366T
915R BK1C0294
920
920 BL