马来酸酐接枝HDPE-g-MAH TY 1053H AMPLIFY 粘合剂用

AMPLIFY™ TY 1053H
Functional Polymer
陶氏塑料
产品说明
AMPLIFY™ TY 1053H Functional Polymer is a maleic anhydride grafted (MAH) polymer concentrate
designed as a blend component for unmodified polyethylene. In tie layers for flexible packaging,
AMPLIFY TY 1053H Functional Polymer promotes adhesion of polyethylene to barrier polymers such
as polyamide and ethylene vinyl alcohol (EVOH). The functionality of this polymer also promotes
adhesion between metal, polyolefins, cellulose, polyester, polycarbonate, glass, and foil.
Typical blending levels in polyethylene let-down resin are 12-20% for EVOH and 6-12% for nylon.
Main Characteristics:
Maleic anhydride modified HDPE
Adhesive concentrate for use in blown, cast, and coating applications
Tie layer for food packaging and pipe coating
Adhesive layer in multi-layer flexible film applications
Polymer compatibilizer
Complies with:
U.S. FDA 21 CFR 177.1520(c)6
EU, No 10/2011
Consult the regulations for complete details.
基本信息
机构评级FDA 21 CFR 177.1520(c) 6 欧洲 No 10/2011
形式粒子
物理性能额定值单位制测试方法
密度 0.958 g/cm³ ASTM D792
熔流率(熔体流动速率) (190°C/2.16 kg) 2.0 g/10 min ASTM D1238, ISO 1133
MAH 接枝水平 1 Very High 内部方法
硬度额定值单位制测试方法
肖氏硬度 ASTM D2240, ISO 868
邵氏 A 98 ASTM D2240, ISO 868
邵氏 D 67 ASTM D2240, ISO 868
机械性能额定值单位制测试方法
抗张强度
断裂 2 15.9 MPa ASTM D638
断裂 15.9 MPa ISO 527-2/51
伸长率
断裂 3 300 % ASTM D638
断裂 300 % ISO 527-2/51
弯曲模量 - 2% 正割 924 MPa ASTM D790A, ISO 178
热性能额定值单位制测试方法
维卡软化温度 129 °C ASTM D1525, ISO 306
溶融温度(DSC) 130 °C 内部方法
补充信息
Molded in accordance with ASTM D4976.
备注
1. Low: 0.5 wt%, Very High >1.0 wt%.
2. 51 mm/min
3. 51 mm/min