PEI的注塑模工艺条件：
熔化温度：普通类型材料为340～400℃；增强类型材料为340～415℃。
模具温度：107～175℃，建议模具温度为140℃。压力：700～1500bar。
速度：使用尽可能高的速度。
干燥处理：PEI具有吸湿特性并可导致材料降解。要求湿度值应小于0.02%。建议干燥条件为150℃、4小时的干燥处理。

Pei has strong high temperature stability, even if it is non reinforced Pei, it still has good toughness and strength. Therefore, Pei can be used to make high temperature heat-resistant devices. Pei also has good flame retardant, chemical resistance and electrical insulation properties. The glass transition temperature is very high, up to 215 ℃. Pei also has low shrinkage and good isotropic mechanical properties. Adding glass fiber, carbon fiber or other fillers can achieve the pure of reinforcement and modification; it can also form heat-resistant polymer alloy with other engineering plastics, which can be used for a long time under the working temperature of - 160 ~ 180 ℃. UL stipulates that the long-term service temperature of polyetherimide resin is 338t and 356t. According to the grade, the combustion grade reaches ul94v-010 mil thickness. The oxygen index is 47, and Pei meets the FAA flame retardant and heat release material standards for aircraft internals. It has a glass transition temperature of 419f and allows intermittent use at 392f, resulting in short-term excursion at higher temperatures.

UL has specified that the long-term service temperature of polyetherimide resin is 338t and 356t (according to grade), and the combustion grade reaches UL94V-0 (10 mil thickness) The oxygen index is 47, and polyetherimide meets the requirements of FAA flame retardant and heat release material standards for aircraft internals. It has a glass transition temperature of 419f and allows intermittent use at 392f, resulting in short-term excursion at higher temperatures. At 356t, the tensile temperature and flexural modulus are above 41 and 2068 MPa respectively. The materials reinforced with glass fiber and carbon fiber have higher strength and stiffness near the glass transition temperature.

Pei plate is an amorphous plastic. It is a kind of amorphous high-performance polymer. It is made of engineering plastics made of amorphous Pei (polyether imide) by high-temperature extrusion of extruder. China Plastics