PEI的注塑模工艺条件：
熔化温度：普通类型材料为340～400℃；增强类型材料为340～415℃。
模具温度：107～175℃，建议模具温度为140℃。压力：700～1500bar。
速度：使用尽可能高的速度。
干燥处理：PEI具有吸湿特性并可导致材料降解。要求湿度值应小于0.02%。建议干燥条件为150℃、4小时的干燥处理。

Pei has strong high temperature stability, even if it is non reinforced Pei, it still has good toughness and strength. Therefore, Pei can be used to make high temperature heat-resistant devices. Pei also has good flame retardant, chemical resistance and electrical insulation properties. The glass transition temperature is very high, up to 215 ℃. Pei also has low shrinkage and good isotropic mechanical properties. Adding glass fiber, carbon fiber or other fillers can achieve the pure of reinforcement and modification; it can also form heat-resistant polymer alloy with other engineering plastics, which can be used for a long time under the working temperature of - 160 ~ 180 ℃. UL stipulates that the long-term service temperature of polyetherimide resin is 338t and 356t. According to the grade, the combustion grade reaches ul94v-010 mil thickness. The oxygen index is 47, and Pei meets the FAA flame retardant and heat release material standards for aircraft internals. It has a glass transition temperature of 419f and allows intermittent use at 392f, resulting in short-term excursion at higher temperatures.

美国保险商实验室规定聚醚树脂的长期使用温度是338T和356T（根据等级），燃烧等级达到UL94V—0（10密耳厚度。）氧指数达47，聚醚酰符合飞机内件要求的FAA阻燃性和热稀放性的材料标准。它的玻璃化转变温度为419F，并允许在392F下间断使用，在更高温度下，产生短期偏移。在356T下，拉伸温度和挠曲模量分别在41和2068MPa以上。用玻纤、碳纤维增强的材料在接近玻璃态转变温度下，具有更高的强度和刚度。

Pei plate is an amorphous plastic. It is a kind of amorphous high-performance polymer. It is made of engineering plastics made of amorphous Pei (polyether imide) by high-temperature extrusion of extruder. China Plastics
Our strengths:
Our products can provide customers with SGS report and COA factory report
Our market information is first-class and accurate
We provide after-sales technical support in time
Our supply is sufficient and stable