深圳全国发货弯钩型钢纤维厂家

钢纤维检测编辑
1、钢纤维的抗拉强度检验，要求其抗拉强度不低于380MPa；
2、钢纤维的抗弯拆性能，钢纤维应能经受直径3㎜钢棒弯拆90°不断，每批次检验不少于10根；
3、杂质含量，钢纤维表面不得有油污，不得镀有有害物质或影响钢纤维与混凝土粘接的杂质；
4、钢纤维的长度偏差不应**过标准长度的10%，每批次至少随机抽查10根以上；
5、钢纤维的直径或等效直径合格率不得低于90%，可采取重量法检验，每批次抽检100根，用天平称量，卡尺测其长度，要求得到的等效平均值满足规定。
原材料的检验：
必须满足上述原材料的质量控制标准，应按照公路工程施工技术规范的要求进行检验。
钢纤维混凝土的检验：
应重点检验钢纤维混凝土的和易性、塌落度和水灰比等，同时必须现场目检钢纤维在混凝土的分布情况，发现有钢纤维结团现象应延长拌和时间。
Steel fiber inspection editor
1. The tensile strength test of steel fiber requires that the tensile strength shall not be less than 380MPa;
2. The bending and dismantling performance of steel fiber shall be able to withstand 90 ° continuous bending and dismantling of steel bar with diameter of 3mm, and no less than 10 pieces shall be inspected in each batch;
3. Impurity content: there shall be no oil stain on the surface of steel fiber, no harmful substances or impurities affecting the bonding between steel fiber and concrete;
4. The length deviation of steel fiber shall not exceed 10% of the standard length, and at least 10 pieces of steel fiber shall be randomly selected for each batch;
5. The qualified rate of steel fiber diameter or equivalent diameter shall not be less than 90%. Weight method can be adopted for inspection. 100 pieces of steel fiber can be sampled for each batch, weighed by balance and measured by caliper. The required equivalent average value meets the requirements.
Inspection of raw materials:
It must meet the quality control standards of the above raw materials, and shall be inspected in accordance with the requirements of the technical specifications for highway engineering construction.
Inspection of steel fiber reinforced concrete:
The workability, slump, water cement ratio, etc. of steel fiber concrete shall be mainly inspected. Meanwhile, the distribution of steel fiber in concrete shall be inspected visually on site. The mixing time shall be prolonged if steel fiber agglomeration is found.

钢纤维问世的时间不长，但应用领域越来越广泛，与此相应，钢纤维的品种也再不断增多。
1.按外形划分（图1）有：平直形钢纤维（a）、压棱形钢纤维（b)、波形钢纤维（c）、弯钩形钢纤维（d\e）、大头形钢纤维（f）、双尖形钢纤维（g）、集束钢纤维（h）等等。
2.按截面形状划分（图2）有：圆形（a）、矩形（b）、槽型（c）、不规则性（d）
3.按生产工艺划分有：切断钢纤维（用细钢丝切断）；剪切钢纤维（用薄钢板、带钢剪切）；
铣削型钢纤维（用厚钢板或钢锭切削）；熔抽钢纤维（用熔融钢水抽制）。有前途的是溶抽钢纤维，价格。
4.按材质划分有：
普碳钢纤维（抗拉强度一般在300~2500MPa）；
不锈钢纤维（按材质有304,310,330,430,446等）；
其他金属纤维（铝纤维、铜纤维、钛纤维以及合金纤维）。5.按表面涂覆状态划分有：
无涂覆层，表面涂环氧树脂，镀锌等。工业上大量使用的是无涂覆层的普通钢纤维。
6.按施工工艺分类有：喷射用、浇注用。
7.按直径尺寸分类有：
普通钢纤维（直径d>0.08mm）；
**细钢纤维（直径d≤0.08mm）；
**细钢纤维主要用于增强塑料及石棉摩擦材料。
Steel fiber has not been out for a long time, but its application field is more and more extensive. Accordingly, the variety of steel fiber is also increasing.
1. According to the shape (Figure 1), there are: straight steel fiber (a), pressed prismatic steel fiber (b), corrugated steel fiber (c), hook shaped steel fiber (D \ E), large head shaped steel fiber (f), double pointed steel fiber (g), bundled steel fiber (H), etc.
2. Divided by section shape (Fig. 2): Circular (a), rectangular (b), groove (c), irregular (d)
3. According to the production process, it can be divided into: cutting off steel fiber (cutting with fine steel wire); cutting steel fiber (cutting with sheet steel and strip steel);
Milling section steel fiber (cutting with thick steel plate or ingot); melting drawing steel fiber (drawing with molten steel). The most promising is the steel fiber with the lowest price.
4. It is divided into:
Ordinary carbon steel fiber (tensile strength is generally 300 ~ 2500mpa);
Stainless steel fiber (304310330430446, etc. according to the material);
Other metal fibers (aluminum fiber, copper fiber, titanium fiber and alloy fiber). 5. According to the surface coating state, it is divided into:
No coating, surface coated with epoxy resin, galvanized, etc. The common steel fiber without coating is widely used in industry.
6. According to the classification of construction technology, it is used for spraying and pouring.
7. Classified by diameter and size:
Ordinary steel fiber (diameter d > 0.08mm);
Ultra fine steel fiber (diameter D ≤ 0.08mm);
Superfine steel fiber is mainly used for reinforcing plastics and asbestos friction materials.

ntroduction to steel fiber
为增强砂浆或混凝土而加入的、长度和直径在一定范围内的细钢丝。常用截面为圆形的长直钢纤维，其长度为10～60毫米，直径为0.2～0.6毫米，长径比为30～100。为增加纤维和砂浆或混凝土的界面粘结，可选用各种异形的钢纤维，其截面有矩形、锯齿形、弯月形的；截面尺寸沿长度而交替变化的；波形的；圆圈状的；端部放大的或带弯钩的等。当使用截面非圆
形的钢纤维时，可按下式计算其当量直径（de)：，
以切断细钢丝法、冷轧带钢剪切、钢锭铣削或钢水快速冷凝法制成长径比（纤维长度与其直径的比值，当纤维截面为非圆形时，采用换算等效截面圆面积的直径）为30～100的纤维。因制取方法的不同钢纤维的性能有很大不同，如冷拔钢丝拉伸强度为380-3000MPa、冷轧带钢剪切法拉伸强度为600-900MPa、钢锭铣削法为700MPa；钢水冷凝法虽为380MPa，但是适合生产耐热纤维。

钢纤维常见生产加工方法
钢纤维薄板剪切法
薄板剪切法是吧冷轧薄钢板切成钢纤维的方法，剪切前用特制的小型纵剪机将薄冷轧卷板剪成带钢卷，带钢卷的宽度和钢纤维的长度相同，然后将带钢卷连续不断地送入旋转或普通冲床切断（如图2-3,b），旋转的轴与薄板进给方向互相垂直。原材料一般采用退火的冷轧钢板，为提高强度也可以使用未退火的冷轧钢板。
.钢锭铣削法
所用原材料为厚钢板或钢锭，用旋转的平刃铁刀进行切削制成的钢纤维（如图2-3）。切削时，钢纤维将产生很的塑性变形，轴间发生扭曲，可以与混凝土等基体的粘结力。若以普通低碳钢为原材料时，切削成的钢纤维经加工硬化后，其弧度约为母材的两倍半，成为一种高强度、高硬度的钢纤维。